5083 ورقة سبائك الألومنيوم VS. 6061 صفائح ألمنيوم معدنية
Similarities Between 5083 and 6061 Aluminum
- High Aluminum Content: Both alloys share approximately 96% of their average alloy composition, making them predominantly aluminum.
- براعه: They are both used in a variety of industries, including marine, automotive, and aerospace, due to their favorable strength-to-weight ratios and corrosion resistance.
aluminum sheet interleaved with
paper
Key Differences Between 5083 and 6061 Aluminum
1. Strength and Heat Treatment
- 5083: This is a non-heat-treatable alloy that relies on work hardening to achieve its strength. It offers excellent performance in extreme environments, particularly at low temperatures.
- 6061: A heat-treatable alloy that can be strengthened through precipitation hardening. The T6 temper of 6061 provides higher strength compared to 5083, making it suitable for structural applications.
5083 H321 aluminum sheet with blue
films
2. المقاومة للتآكل
- 5083: Known for its exceptional resistance to seawater and industrial chemicals, making it ideal for marine applications.
- 6061: Offers good corrosion resistance, especially when anodized, but is generally less resistant than 5083 in marine environments.
3. Weldability
- 5083: Exhibits excellent weldability with minimal loss in strength in the welded areas, which is crucial for shipbuilding and similar applications.
- 6061: While it can be welded, the strength in the heat-affected zones can be reduced, and post-weld heat treatment may be necessary to restore properties.
4. آلية
- 5083: More challenging to machine due to its work-hardened state, which can lead to increased tool wear.
- 6061: Offers excellent machinability, especially in the T6 temper, making it a preferred choice for components requiring precise machining.
5. التطبيقات
- 5083: Commonly used in marine environments, pressure vessels, and cryogenic applications due to its strength and corrosion resistance.
- 6061: Widely used in aerospace, automotive, and structural applications where higher strength and good machinability are required.
5083 تطبيق ورقة سبائك الألومنيوم
- بناء سفن الغاز الطبيعي المسال
- أوعية الضغط
- صهاريج التخزين
- الهياكل الملحومة (قوة عالية)
- درع
- منصات الحفر
6061 تطبيق ورقة سبائك الألومنيوم
- تجهيزات الطائرات ، وحوامل عدسات الكاميرا ، والوصلات ، والتركيبات والأجهزة البحرية ، والتركيبات والوصلات الكهربائية ، والزخرفية أو المتنوعة.
- الأجهزة ، دبابيس المفصلات ، الأجزاء المغناطيسية ، مكابس الفرامل ، المكابس الهيدروليكية ، تجهيزات الأجهزة ، الصمامات وأجزاء الصمام.
Comparative Overview
| خاصية | 5083 Aluminum | 6061 Aluminum |
| Heat Treatable | رقم | Yes (e.g., T6, T651 tempers) |
| قوة الشد | Moderate | Higher (especially in T6 temper) |
| المقاومة للتآكل | Excellent (especially in seawater) | Good |
| Weldability | ممتاز | Good (may require post-weld treatment) |
| آلية | Fair | ممتاز |
| Typical Applications | Marine, cryogenics, pressure vessels | Aerospace, automotive, structural components |
خاتمة
Choosing between 5083 and 6061 aluminum alloys depends on the specific requirements of your application:
- Opt for 5083 when corrosion resistance, especially in marine environments, and excellent weldability are paramount.
- Choose 6061 when higher strength and superior machinability are needed, such as in aerospace or structural applications.
Understanding these differences ensures the selection of the appropriate alloy for your project’s needs.
ملحوظة: For detailed specifications and material properties, always refer to the manufacturer’s datasheets or consult with a materials engineer.
chemical composition
| درجة | ماكس (%) | ||||||||||
| سي | الحديد | النحاس | مينيسوتا | ملغ | سجل تجاري | Zn | تي | آحرون: كل |
آحرون: المجموع |
Al: مين. | |
| سبيكة 5083 | 0.40 | 0.40 | 0.10 | 0.4~1.0 | 4.0~4.9 | 0.05~0.25 | 0.25 | 0.15 | 0.05 | 0.15 | بقية |
More detail of 5083 aluminum
sheet/plate
عبوات صفائح الألمنيوم
| سبيكة | سي | الحديد | النحاس | مينيسوتا | ملغ | سجل تجاري | Zn | تي | آحرون: كل |
آحرون: المجموع |
Al: مين. |
| 6061 | 0.40~0.8 | 0.70 | 0.15~0.4 | 0.15 | 0.8~1.2 | 0.04~0.35 | 0.25 | 0.15 | 0.05 | 0.15 | بقية |
More detail of 6061
aluminum sheet and plate
مواصفات لوح صفائح الألمنيوم 5083 و لوح الألمنيوم 6061
| البعد | نطاق |
| سماكة | 0.5 ~ 6.0 مم للورق ، 500 مم كحد أقصى |
| عرض | 600 ~ 2650 ملم |
- - العرض والطول القياسيين: 4〃 x 8〃, 4“ x 4“ , 4 in. x 10 in. aluminum sheet, 5 x 10 aluminum
sheet, 48‘ x 96’ aluminum sheet, 1219 * 2438mm, 1220mm x 2440mm aluminum sheet, 1000mm x 2000mm aluminum sheet,
1250mm x 2500mm, 1219 x 2438mm, 1524 x 3048mm, 1500mm x 3000mm aluminum sheet. - - صقل الأسطح: مطحنة الانتهاء (ما لم ينص على خلاف ذلك) ، اللون المطلي ، أو الجص منقوش
- - حماية السطح: ورق مشذب ، تصوير PE / PVC (إذا تم تحديده)
- - أقل كمية ممكن طلبها: 3MT
بالإضافة إلى المواصفات الشائعة الاستخدام ، يمكن لـ Tigers Aluminium أيضًا إنتاج 5052 صفائح ألمنيوم عريضة للغاية وسميكة للغاية مع تخفيف الضغط الداخلي وعدم حدوث تشوه أثناء القطع ، والعرض 2650 مم ، وسمك 500 مم.
الفرق بين سبائك 6061 وسبائك أخرى
مختلفة مع سبائك الألومنيوم 5052
يحتوي كل من الألومنيوم 5052 و 6061 على المغنيسيوم كعنصر أساسي في صناعة السبائك. في حالة 5052 ، هو عنصر السبائك الأساسي الوحيد. 6061 يحتوي على السيليكون أيضًا. تتمثل إحدى الفوائد الرئيسية لهذه السبيكة في مستواها العالي من قابلية اللحام مقارنةً بالسبائك الأخرى. بالنسبة للمشاريع التي تكون فيها قابلية اللحام هي المفتاح ، فإن الأمر يستحق النظر فيه.
ومع ذلك ، فإن أحد الجوانب السلبية لـ 5052 هو أنه لا يمكن معالجته بالحرارة. إنه جيد لمجموعة متنوعة من تطبيقات اللحام ويعمل بشكل جيد في التطبيقات البحرية بسبب مقاومته العالية للتآكل.
وصف 5083 و 6061 على ويكيبيديا ：
المحتوى أعلاه هو الفرق بين سبائك الألومنيوم 5083 و 6061 سبائك الألومنيوم.
Most of aluminum 5083 sheet/plate and 6061 aluminum plate stock is available in full size and custom cut lengths.