5083 folha de liga de alumínio VS. 6061 chapas de metal de alumínio
A liga de alumínio 5083 e as chapas de alumínio 6061 são ambas ligas de alumínio, com diferentes componentes metálicos e diferentes resistências. Eles são comumente usados em navios, blindagens de veículos e acessórios de aeronaves.

5083 folha de liga de alumínio VS. 6061 chapas de metal de alumínio

rating:

Similarities Between 5083 and 6061 Aluminum

  • High Aluminum Content: Both alloys share approximately 96% of their average alloy composition, making them predominantly aluminum.​
  • Versatilidade: They are both used in a variety of industries, including marine, automotive, and aerospace, due to their favorable strength-to-weight ratios and corrosion resistance.
folha de alumínio intercalada com papel

aluminum sheet interleaved with
paper

Key Differences Between 5083 and 6061 Aluminum

1. Strength and Heat Treatment

  • 5083: This is a non-heat-treatable alloy that relies on work hardening to achieve its strength. It offers excellent performance in extreme environments, particularly at low temperatures.​
  • 6061: A heat-treatable alloy that can be strengthened through precipitation hardening. The T6 temper of 6061 provides higher strength compared to 5083, making it suitable for structural applications.
5083 H321 folha de alumínio com filmes azuis

5083 H321 aluminum sheet with blue
films

2. Resistência à corrosão

  • 5083: Known for its exceptional resistance to seawater and industrial chemicals, making it ideal for marine applications.​
  • 6061: Offers good corrosion resistance, especially when anodized, but is generally less resistant than 5083 in marine environments.​

3. Weldability

  • 5083: Exhibits excellent weldability with minimal loss in strength in the welded areas, which is crucial for shipbuilding and similar applications.​
  • 6061: While it can be welded, the strength in the heat-affected zones can be reduced, and post-weld heat treatment may be necessary to restore properties.​

4. Maquinabilidade

  • 5083: More challenging to machine due to its work-hardened state, which can lead to increased tool wear.​
  • 6061: Offers excellent machinability, especially in the T6 temper, making it a preferred choice for components requiring precise machining.​

5. Formulários

  • 5083: Commonly used in marine environments, pressure vessels, and cryogenic applications due to its strength and corrosion resistance.​
  • 6061: Widely used in aerospace, automotive, and structural applications where higher strength and good machinability are required.

aplicação de folha de liga de alumínio 5083

  • construção de navios de GNL
  • Vasos de pressão
  • Tanques de armazenamento
  • Estruturas soldadas (alta resistência)
  • Placa de armadura
  • Sondas de perfuração

Aplicação de folha de liga de alumínio 6061

  • Acessórios para aeronaves, montagens de lentes de câmeras, acoplamentos, acessórios e ferragens para fuzileiros navais, acessórios e conectores elétricos, decorativos ou diversos.
  • ferragens, pinos de dobradiça, peças de magneto, pistões de freio, pistões hidráulicos, acessórios para eletrodomésticos, válvulas e peças de válvulas.

Comparative Overview

Propriedade 5083 Aluminum 6061 Aluminum
Heat Treatable Não Yes (e.g., T6, T651 tempers)
Resistência à tração Moderate Higher (especially in T6 temper)
Resistência à corrosão Excellent (especially in seawater) Good
Weldability Excelente Good (may require post-weld treatment)
Maquinabilidade Fair Excelente
Typical Applications Marine, cryogenics, pressure vessels Aerospace, automotive, structural components

Conclusão

Choosing between 5083 and 6061 aluminum alloys depends on the specific requirements of your application:​

  • Opt for 5083 when corrosion resistance, especially in marine environments, and excellent weldability are paramount.​
  • Choose 6061 when higher strength and superior machinability are needed, such as in aerospace or structural applications.​

Understanding these differences ensures the selection of the appropriate alloy for your project’s needs.

Observação: For detailed specifications and material properties, always refer to the manufacturer’s datasheets or consult with a materials engineer.

chemical composition

5083 composição química de folha/placa de alumínio

Grau Máx. (%)
Si Fe Cu Mn Mg Cr Zn Ti Outras:
Cada
Outras:
Total
Al: Min.
liga 5083 0.40 0.40 0.10 0.4~1.0 4.0~4.9 0.05~0.25 0.25 0.15 0.05 0.15 restante

More detail of 5083 aluminum
sheet/plate

 

pacotes de folha de alumínio

pacotes de chapa de alumínio

 

6061 aluminum sheet / plate Chemical
Composition (For Reference)

Liga Si Fe Cu Mn Mg Cr Zn Ti Outras:
Cada
Outras:
Total
Al: Min.
6061 0.40~0.8 0.70 0.15~0.4 0.15 0.8~1.2 0.04~0.35 0.25 0.15 0.05 0.15 restante

More detail of 6061
aluminum sheet and plate

Especificação de chapa de alumínio 5083 e chapa de alumínio 6061

Folha/placa/bobina de alumínio Faixa de tamanhos disponíveis

Dimensão Variedade
Grossura 0,5 ~ 6,0 mm para folha, máx. 500 mm
Largura 600 ~ 2.650 mm
  • – Largura e Comprimento Padrão: 4〃 x 8〃, 4“ x 4“ , 4 in. x 10 in. aluminum sheet, 5 x 10 aluminum
    sheet, 48‘ x 96’ aluminum sheet, 1219 * 2438mm, 1220mm x 2440mm aluminum sheet, 1000mm x 2000mm aluminum sheet,
    1250mm x 2500mm, 1219 x 2438mm, 1524 x 3048mm, 1500mm x 3000mm aluminum sheet.
  • – Acabamento de superfície: Acabamento do moinho (a menos que especificado de outra forma), Revestido de Cor ou Estuque Em Relevo
  • – Proteção da superfície: Papel intercalado, filmagem de PE/PVC (se especificado)
  • – Quantidade mínima de pedido: 3MT

Além das especificações comumente usadas, a Tigers Aluminium também pode produzir 5052 placas de alumínio ultra largas e ultra grossas com alívio de tensão interno e sem deformação durante o corte, e a largura é de 2650 mm, a espessura é de 500 mm.

A diferença entre a liga 6061 e outras ligas

diferente com liga de alumínio 5052

5052 alumínio e 6061 tem magnésio como elemento de liga primário. No caso do 5052, é o único elemento de liga primária. 6061 também tem silício. Um dos principais benefícios desta liga é seu alto nível de soldabilidade em comparação com outras ligas. Para projetos onde a soldabilidade é fundamental, vale a pena considerar.

Uma desvantagem do 5052, porém, é que ele não é tratável termicamente. É bom para uma variedade de aplicações de soldagem e funciona bem em aplicações marítimas devido à sua alta resistência à corrosão.

Descrição de 5083 e 6061 na wikipedia:

5083 alumínio na wikipedia

6061 alumínio na wikipedia

O conteúdo acima é a diferença entre a liga de alumínio 5083 e a liga de alumínio 6061.

Most of aluminum 5083 sheet/plate and 6061 aluminum plate stock is available in full size and custom cut lengths.

 